Ah, I was following the logic that I should get as much penetration as possible to ensure the welds were as strong as the Hardox itself, but that seems redundant if I'm weakening it in the process. Am I best off doing short welds at a couple of points along each length then do you reckon? That with some support brackets behind shouldn't create so much heat